    PC LR200G2 沙伯基础创新
    2017-07-21 15:23:24   来源:   评论:0 点击:

    PC LR200G2 沙伯基础创新


    产品描述

    LEXAN PC LR200G2 沙伯基础创新 物性表

    REMEX LR200G2 is a 20 % glass fibre reinforced material used for non-cosmetic injection moulding applications.
    TYPICAL PROPERTIES (1)
    MEC HANICAL机械性能
    Value Unit Standard
    Tensile Stress, break, 5 mm/min / 抗张程度,断裂,5mm/min
    80
    MPa
    ISO 527
    Tensile Stress, yield 50 mm/min / 抗张程度,屈服, 50 mm/min
    60
    MPa
    ISO 527
    Tensile Stress, break, 50 mm/min / 抗张程度,断裂,50mm/min
    54
    MPa
    ISO 527
    Tensile Strain, break, 5 mm/min / 拉伸伸长,断裂,5mm/min
    2
    %
    ISO 527
    Tensile Strain, yield, 50 mm/min / 拉伸伸长,屈服,,50mm/min
    4
    %
    ISO 527
    Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min
    5000
    MPa
    ISO 527
    Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min
    100
    MPa
    ISO 178
    Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min
    4500
    MPa
    ISO 178
    Hardness, H358/30 / 球压硬度,H358/30
    115
    MPa
    ISO 2039-1
    IMPACT
    Value Unit Standard
    Izod Impact, unnotched 80*10*4 +23°C
    25
    kJ/m²
    ISO 180/1U
    Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm / 简支梁缺口冲击强度,23°C,C80*10*4 sp=62mm
    14
    kJ/m²
    ISO 179/1eA
    Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm
    NB
    kJ/m²
    ISO 179/1eU
    THERMAL
    Value Unit Standard
    CTE, 23°C to 80°C, flow
    2.5E-05
    1/°C
    ISO 11359-2
    CTE, 23°C to 80°C, xflow
    7.5E-05
    1/°C
    ISO 11359-2
    Vicat Softening Temp, Rate B/120 / 维卡软化温度,B级/120
    150
    °C
    ISO 306
    HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm / 热变形温度,1.8 MPa, 未退火, 100 mm 跨距
    126
    °C
    ISO 75/Ae
    PHYSICAL
    Value Unit Standard
    Mold Shrinkage on Tensile Bar, flow (2) / 收缩率,流动
    0.2 – 0.6
    %
    SABIC Method
    Density/密度
    1.35
    g/cm³
    ISO 1183
    Water Absorption, (23°C/sat) / 吸水率, (23°C/sat)
    0.3
    %
    ISO 62
    Moisture Absorption (23°C / 50% RH) / 吸水率, 平衡,(23°C / 50% RH)
    0.12
    %
    ISO 62
    Melt Volume Rate, MVR at 300°C/1.2 kg
    6
    cm³/10 min
    ISO 1133
    ELECTRICAL
    Value Unit Standard
    Surface Resistivity, ROA / 表面电阻率
    2.6E+15
    Ohm
    IEC 60093
    Dielectric Strength, in oil, 3.2 mm / 耐电强度,在油中,3.2mm
    16.4
    kV/mm
    IEC 60243-1
    FLAME CHARACTERISTICS
    Value Unit Standard
    UL Recognized, 94V-0 Flame Class Rating (3) / UL认可,94V-0 阻燃等级(3)
    1.7
    mm
    UL 94
    Source GMD, last updated:08/07/1996
    Processing
     
    Parameter
    Injection Molding
    Value Unit
    Drying Temperature / 干燥温度
    120
    °C
    Drying Time / 干燥时间
    2 – 4
    hrs
    Maximum Moisture Content / 最大含湿量
    0.02
    %
    Melt Temperature / 熔体温度
    290 – 320
    °C
    Nozzle Temperature / 注嘴温度
    280 – 310
    °C
    Front – Zone 3 Temperature / 前区3温度
    290 – 320
    °C
    Middle – Zone 2 Temperature / 中区2温度
    280 – 310
    °C
    Rear – Zone 1 Temperature / 后区1温度
    270 – 300
    °C
    Hopper Temperature / 料筒温度
    60 – 80
    °C
    Mold Temperature / 模具温度
    80 – 120
    °C