    PC BE2130 I沙伯基础创新
    2017-07-21 10:42:11   来源:   评论:0 点击:

    PC BE2130 I沙伯基础创新


    产品描述

    LEXAN PC BE2130 I沙伯基础创新物性表

    FOR EXISTING APPLICATIONS ONLY. High flow, excellent flame rating, standard gloss. Durable, good cost-to- performance balance. Excellent for computer cabinetry and enclosures.
    TYPICAL PROPERTIES (1)

    MECHANICAL机械性能
    Value Unit Standard
    Tensile Stress, yld, Type I, 50 mm/min / 抗拉强度,屈服,类型I,50 mm/min
    62
    MPa
    ASTM D 638
    Tensile Stress, brk, Type I, 50 mm/min / 抗拉强度, 断裂, 类型I, 50 mm/min
    49
    MPa
    ASTM D 638
    Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距
    93
    MPa
    ASTM D 790
    Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距
    2200
    MPa
    ASTM D 790
    IMPACT
    Value Unit Standard
    Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C
    267
    J/m
    ASTM D 256
    Gardner, 23°C
    9
    J
    ASTM D 3029
    Instrumented IMPACT Energy @ peak / 仪表控制抗冲击能量 @ 峰值, 23°C
    47
    J
    ASTM D 3763
    THERMAL
    Value Unit Standard
    HDT, 1.82 MPa, 6.4 mm, unannealed / 热变形温度,1.82 MPa, 6.4 mm, 未退火
    129
    °C
    ASTM D 648
    Relative Temp Index, Elec / 相对热指数, 电性能
    125
    °C
    UL 746B
    Relative Temp Index, Mech w/impact / 相对热指数,机械冲击性能
    110
    °C
    UL 746B
    Relative Temp Index, Mech w/o impact / 相对热指数,非机械冲击性能
    125
    °C
    UL 746B
    PHYSICAL
    Value Unit Standard
    Specific Gravity/比重
    1.21
    ASTM D 792
    Mold Shrinkage, flow, 3.2 mm / 模塑收缩量,流动,3.2 mm
    0.6 – 0.8
    %
    SABIC Method
    Melt Flow Rate / 熔流率, 300°C/1.2 kgf / 熔流率,300°C/1.2 kgf
    25
    g/10 min
    ASTM D 1238
    OPTICAL
    Value Unit Standard
    Gloss, untextured, 60 degrees / 光泽度,无纹理,60度
    90
    ASTM D 523
    Gloss, textured, 60 deg, MT-1055-2
    14
    ASTM D 523
    ELECTRICAL
    Value Unit Standard
    Arc Resistance, Tungsten {PLC} / 耐电弧性{PLC}
    7
    PLC Code
    ASTM D 495
    Hot Wire Ignition {PLC) / 热丝引燃 {PLC)
    2
    PLC Code
    UL 746A
    High Voltage Arc Track Rate {PLC} / 高电压电弧起痕速率
    4
    PLC Code
    UL 746A
    High Ampere Arc Ign, surface {PLC} / 高电流电弧引燃,表面{PLC}
    3
    PLC Code
    UL 746A
    Comparative Tracking Index (UL) {PLC} / 漏电起痕指数 (UL) {PLC}
    2
    PLC Code
    UL 746A
    FLAME CHARACTERISTICS
    Value Unit Standard
    UL Recognized, 94V-0 Flame Class Rating (3) / UL认可,94V-0 阻燃等级(3)
    1.47
    mm
    UL 94
    UL Recognized, 94-5VA Rating (3) / UL认可,94-5VA 阻燃等级(3)
    2.99
    mm
    UL 94
    Source GMD, last updated:01/09/2003
    Processing
     
    Parameter
    Injection Molding
    Value Unit
    Drying Temperature / 干燥温度
    120
    °C
    Drying Time / 干燥时间
    3 – 4
    hrs
    Drying Time (Cumulative) / 干燥时间(累积的)
    48
    hrs
    Maximum Moisture Content / 最大含湿量
    0.02
    %
    Melt Temperature / 熔体温度
    270 – 295
    °C
    Nozzle Temperature / 注嘴温度
    265 – 290
    °C
    Front – Zone 3 Temperature / 前区3温度
    270 – 295
    °C
    Middle – Zone 2 Temperature / 中区2温度
    260 – 280
    °C
    Rear – Zone 1 Temperature / 后区1温度
    250 – 270
    °C
    Mold Temperature / 模具温度
    70 – 95
    °C
    Back Pressure / 背压
    0.3 – 0.7
    MPa
    Screw Speed / 螺杆速度
    40 – 70
    rpm
    Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比
    40 – 60
    %
    Vent Depth / 排气孔深度
    0.025 – 0.076
    mm
    Source GMD, last updated:01 /09/2017 www.tpeepch.com