LEXAN PC PD4003 沙伯基础创新 物性表
LEXAN PD4003 is a high heat resistant poly(ester)carbonate injection moulding resin. All properties stated below have been measured on black material.
| TYPICAL PROPERTIES (1) | |||
|
MECHANICAL机械性能
|
Value | Unit | Standard |
|
Tensile Stress, yield 50 mm/min / 抗张程度，屈服, 50 mm/min
|
65
|
MPa
|
ISO 527
|
|
Tensile Stress, break, 50 mm/min / 抗张程度,断裂,50mm/min
|
60
|
MPa
|
ISO 527
|
|
Tensile Strain, yield, 50 mm/min / 拉伸伸长,屈服,,50mm/min
|
6
|
%
|
ISO 527
|
|
Tensile Strain, break, 50 mm/min / 拉伸伸长,断裂,50mm/min
|
85
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min
|
2150
|
MPa
|
ISO 527
|
|
Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min
|
100
|
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min
|
2300
|
MPa
|
ISO 178
|
|
Hardness, H358/30 / 球压硬度，H358/30
|
105
|
MPa
|
ISO 2039-1
|
|
THERMAL
|
Value | Unit | Standard |
|
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
|
160
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/120 / 维卡软化温度,B级/120
|
162
|
°C
|
ISO 306
|
|
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm / 热变形温度，0.45 MPa, 未退火, 100 mm 跨距
|
155
|
°C
|
ISO 75/Be
|
|
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm / 热变形温度，1.8 MPa, 未退火, 100 mm 跨距
|
142
|
°C
|
ISO 75/Ae
|
|
PHYSICAL
|
Value | Unit | Standard |
|
Density/密度
|
1.2
|
g/cm³
|
ISO 1183
|
|
Melt Volume Rate, MVR at 300°C/5.0 kg
|
20
|
cm³/10 min
|
ISO 1133
|
|
Source GMD, last updated:10/16/2001
|
|
Processing
|
| Parameter | ||
|
Injection Molding
|
Value | Unit |
|
Drying Temperature / 干燥温度
|
125 – 135
|
°C
|
|
Drying Time / 干燥时间
|
3 – 4
|
hrs
|
|
Melt Temperature / 熔体温度
|
325 – 360
|
°C
|
|
Nozzle Temperature / 注嘴温度
|
320 – 340
|
°C
|
|
Front – Zone 3 Temperature / 前区3温度
|
320 – 340
|
°C
|
|
Middle – Zone 2 Temperature / 中区2温度
|
310 – 330
|
°C
|
|
Rear – Zone 1 Temperature / 后区1温度
|
300 – 320
|
°C
|
|
Hopper Temperature / 料筒温度
|
60 – 80
|
°C
|
|
Mold Temperature / 模具温度
|
100 – 125
|
°C
|
|
Source GMD, last updated:10/16/2017长汇塑料代理
|