    LEXAN PC 4301 
    沙伯基础 物性表

    Lexan 4301 is a high heat resistant poly (ester) carbonate resin for injection molding
    TYPICAL PROPERTIES (1)
    MECHANICAL机械性能
    Value Unit Standard
    Tensile Stress, yld, Type I, 50 mm/min / 抗拉强度,屈服,类型I,50 mm/min
    64
    MPa
    ASTM D 638
    Tensile Stress, brk, Type I, 50 mm/min / 抗拉强度, 断裂, 类型I, 50 mm/min
    69
    MPa
    ASTM D 638
    Tensile Strain, yld, Type I, 50 mm/min / 拉伸伸长, 屈服, 类型I, 50 mm/min
    7
    %
    ASTM D 638
    Tensile Strain, brk, Type I, 50 mm/min / 拉伸伸长,断裂,类型I, 50 mm/min
    >50
    %
    ASTM D 638
    Tensile Modulus, 5 mm/min / 拉伸模量,5 mm/min
    2100
    MPa
    ASTM D 638
    Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距
    95
    MPa
    ASTM D 790
    Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距
    2200
    MPa
    ASTM D 790
    Tensile Stress, yield 50 mm/min / 抗张程度,屈服, 50 mm/min
    65
    MPa
    ISO 527
    Tensile Stress, break, 50 mm/min / 抗张程度,断裂,50mm/min
    60
    MPa
    ISO 527
    Tensile Strain, yield, 50 mm/min / 拉伸伸长,屈服,,50mm/min
    6
    %
    ISO 527
    Tensile Strain, break, 50 mm/min / 拉伸伸长,断裂,50mm/min
    85
    %
    ISO 527
    Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min
    2150
    MPa
    ISO 527
    Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min
    100
    MPa
    ISO 178
    Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min
    2300
    MPa
    ISO 178
    IMPACT
    Value Unit Standard
    Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C
    600
    J/m
    ASTM D 256
    Izod IMPACT, notched, -30°C / 悬壁梁缺口冲击强度, -30°C
    125
    J/m
    ASTM D 256
    Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量,23°C
    120
    J
    ASTM D 3763
    Izod IMPACT, unnotched 80*10*3 +23°C
    NB
    kJ/m²
    ISO 180/1U
    Izod IMPACT, unnotched 80*10*3 -30°C
    NB
    kJ/m²
    ISO 180/1U
    Izod IMPACT, notched 80*10*3 +23°C / 悬壁梁缺口冲击强度, 80*10*3 +23°C
    45
    kJ/m²
    ISO 180/1A
    Izod IMPACT, notched 80*10*3 -30°C / 悬壁梁缺口冲击强度, 80*10*3 -30°C
    11
    kJ/m²
    ISO 180/1A
    Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm / 简支梁缺口冲击强度,23°C,C80*10*3 sp=62mm
    50
    kJ/m²
    ISO 179/1eA
    Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm / 简支梁缺口冲击强度,-30°C,C80*10*3 sp=62mm
    12
    kJ/m²
    ISO 179/1eA
    Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm
    NB
    kJ/m²
    ISO 179/1eU
    Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm
    NB
    kJ/m²
    ISO 179/1eU
    THERMAL
    Value Unit Standard
    Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
    162
    °C
    ASTM D 1525
    HDT, 1.82 MPa, 3.2mm, unannealed / 热变形温度,1.82 MPa, 3.2mm,未退火
    139
    °C
    ASTM D 648
    CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动
    8.E-05
    1/°C
    ASTM E 831
    CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向
    8.E-05
    1/°C
    ASTM E 831
    CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动
    8.E-05
    1/°C
    ISO 11359-2
    CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向
    8.E-05
    1/°C
    ISO 11359-2
    Ball Pressure Test, 125°C +/- 2°C
    pass
    IEC 60695-10-2
    Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
    151
    °C
    ISO 306
    Vicat Softening Temp, Rate B/120 / 维卡软化温度,B级/120
    153
    °C
    ISO 306
    HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm / 热变形温度,1.8 MPa, 未退火,80*10*4, 64.0 mm 跨距
    134
    °C
    ISO 75/Af
    PHYSICAL
    Value Unit Standard
    Specific Gravity/比重
    1.2
    ASTM D 792
    Mold Shrinkage, flow, 3.2 mm / 模塑收缩量,流动,3.2 mm
    0.6 – 0.8
    %
    SABIC Method
    Melt Flow Rate / 熔流率, 300°C/1.2 kgf / 熔流率,300°C/1.2 kgf
    8
    g/10 min
    ASTM D 1238
    Density/密度
    1.2
    g/cm³
    ISO 1183
    Water Absorption, (23°C/sat) / 吸水率, (23°C/sat)
    0.16
    %
    ISO 62
    Moisture Absorption (23°C / 50% RH) / 吸水率, 平衡,(23°C / 50% RH)
    0.35
    %
    ISO 62
    Melt Volume Rate, MVR at 330°C/2.16kg
    40
    cm³/10 min
    ISO 1133
    Source GMD, last updated:11/08/2004
    Processing
     
    Parameter
    Injection Molding
    Value Unit
    Drying Temperature / 干燥温度
    120
    °C
    Drying Time / 干燥时间
    2 – 4
    hrs
    Melt Temperature / 熔体温度
    300 – 330
    °C
    Mold Temperature / 模具温度
    100 – 120
    °C